Infrared spectroscopy showed characteristic peaks of cardanol (2920 cm⁻¹ and 2850 cm⁻¹), indicating successful incorporation into the resin molecular chain.
Thermogravimetric analysis showed a 12% reduction in mass loss rate of the modified resin between 100-300℃.
Differential scanning calorimetry determined that the glass transition temperature increased to 185℃.